NOMINAL COMPOSITION %
|
|
TYPICAL MECHANICAL
PROPERTIES |
| Arsenic |
0.15 - 0.50 |
| Phosphorus |
0.013 - 0.050 |
| Copper |
REM |
|
|
| Tensile Strength |
275 N/mm² |
| 0.2% Proof Stress |
185 N/mm² |
| Elongation |
20 % |
| Hardness |
80 HV |
|
|
TYPICAL PHYSICAL PROPERTIES
|
|
FABRICATION PROPERTIES |
| Density |
8.9 g/cm3 |
| Melting Range |
1053 - 1082 ºC |
| Specific heat |
0.1 cal/g°C |
| Coeff of Thermal Expansion |
0.000017 /ºC |
| Thermal Conductivity |
250-300 W/mºC |
| Electrical Conductivity |
35-40 % IACS |
| Modulus of Elasticity |
13500 N/mm2 |
|
|
| Hot Formability |
Good |
| Cold Formability |
Excellent |
| Machinability Rating |
25(Free cutting brass = 100) |
| Joining Methods: |
|
| Soldering |
Excellent |
| Brazing |
Excellent |
| MIG Welding |
Excellent |
| TIG Welding |
Excellent |
| Resistance Welding |
Good |
|